Fluxtri Salts

It is an economical galvanizing preparation which is used in hot dip galvanizing processes. It has three salts, making the steel or casting surfaces to be brighter.

Blaphoric U 91 (Black Oxide Product)

Iron, steel and casting surfaces are used for coating with oxide layer. Bath installation is done with 70-90% by weight. The product is in powder form, the blacking salt is added slowly to warm water. Bathroom operating temperature is between 135 – 145 0C. When the temperature drops below 1350C, blacking salt is added. After…

Blaphoric U 22 (Black Phosphate Coating)

It is used to coat iron, steel and casting surfaces with black phosphate layer. The bath runs at boiling temperature. The processing time is between 5 and 15 minutes. Parts must be cleaned in degreasing and rüşt removing baths before taking black phosphate treatment. After the oxidation process, the parts are rinsed and taken to…

Passivation

The main purpose of treating hot-dip galvanized parts in passivation ponds after galvanizing is to prevent white oxidation and to prevent corrosion until it goes to the customer and to maintain product brightness.

Phoric Ak 5 (Activator Product)

Manganese is used to form a homogeneous, tight and smooth coating on steel, iron and cast surfaces used before phosphate coating. In order for the product to work effectively, the bath must be mixed with methods such as continuous ventilation. Installation amount is 7-11 g / Liter (0.7% – 1.1%) It works at ambient temperature,…

Phoric T 500 (Manganese Phosphate Coating)

Installation at a concentration of 15% by weight, operating at 85-95 0C, processing time is about 5 to 10 minutes. Used for iron, steel and cast parts. The actuator must be used together with the product (PHORIC AK 5). The parts coated in the acid baths that left unneccesarily too much,  create thick manganese phosphate…

Vibra Cop 01

It is an acidic product that is suitable for degreasing, deburring ans tip correction on iron, steel, aluminum, brass, copper and zamak. It is designed to be used in vibration machines and centrifuge type machines at 2% -5%.

Vibra Brighter 03

It is used in vibration machines for polishing zinc and copper parts. The surfactants in the content provide a degreasing effect. Application is made with polishing stones. A concentration of 2% -3 will be sufficient for brightness. After the process, the surface is covered with a thin film layer and provides resistance to corrosion. The…

Phoric 2 Be (Tube Drawing Zinc Phosphate)

It is produced for thick zinc phosphate coating of tubes before tube drawing operations. Activation bath must be used before zinc phosphate bath to form a homogeneous and tight zinc phosphate layer. After the phosphate coating, we recommend the special type of lubricants according to the tube type. It is used for zinc phosphate coating…